DESCRIPTION

Basic Info.

Model NO.	pipe
Function	Abrasive Resistance
Sample Time	5-8days
Bulk Density	>3.6
Loss Bulk	<0.25
Compressive Strength(MPa)	>1050
Bending Strength(MPa)	>220
Transport Package	as Your Requirement
Specification	Customized
Trademark	Titan
Origin	Shandong, China
HS Code	690912

Product Description

DescriptionCeramic patch elbow, elbow, lined with ceramic patch elbow. The elbow is very different from the traditional production process, and the pipe produced by the self-propagating technology has the organizational structure. The structure of the pipeline determines the comprehensive performance, it is not only wear resistance, corrosion resistance, high temperature resistance, high hardness and strength, but also has a good resistance to mechanical impact and thermal impact of the comprehensive performance.FeaturesSuper wear-resistant, high density: 95% high content chromium corundum ceramic sheet, 100 tons of dry pressing;Elbow integrated hot bending, the outer bending part without seams, easy to wear, prolong the overall life of wear-resistant ceramic elbow;Adhesion firm does not fall off: using high strength modified viscose and staggered joint paste process, no linear gap;High temperature resistance and aging resistance: abandon the traditional organic viscose, using fiber modified formula, good aging resistance;High pressure resistance: using 20# integrated hot bend pipe, can resist high pressure, avoid weld leakage;Smooth inner wall, smooth material: steel parts using seamless forming, smooth inner wall, conducive to reduce wear; At the same time, the height difference between the ceramics is within 0.5mm, smooth and flat.ApplicationWidely distributed in thermal power, iron and steel, smelting, cement, machinery, coal, mining, chemical industry, port and other serious wear industries.
Technical Data

Series	BM92	BMG95	BME95	BMZTA	BMZR
AL2O3 (%)	92±0.5	95±0.5	95±0.5	≥75	-
ZrO2 (%)	-	-	-	≥21	94.8±0.5
Bulk density(g/cm3)	≥3.6	≥3.65	≥3.7	≥4.1	≥5.9
Compressive strength (MPa)	≥1050	≥1300	≥1600	≥2000	-
Bending strength (MPa)	≥220	≥250	≥300	≥400	≥800
Fracture toughness (MPam1/2)	≥3.70	≥3.80	≥4.0	≥4.5	≥7
Rockwell hardness (HRA)	≥82	≥85	≥88	≥90	≥88
Loss bulk (cm3)	≤0.25	≤0.2	≤0.15	≤0.05	≤0.02